Welding Consumables

Leading Supplier of Welding Consumables such as SAW Wire & Flux Products, Flux Cored Wires, Solid Co2/MIG Wire, Stainless Steel Flux Cored Wires and Electrodes from Navi Mumbai.

Flux Cored Wire(FCAW)

Hyundai Brand

SF-71

Property Applications
All position welding of building, shipbuilding, bridges, machinery and vehicles.

Characteristics on Usage
SF-71 is a titania type flux cored wire for all position welding with CO??. Compared with solid wire, spatter loss is low, bead appearance is beautiful and arc is soft with good stability. Slag covering is uniform with good removal.

Notes on Usage
1. Proper preheating(50~150??C)(122~302??F) and interpass temperature must be used in order to release hydrogen which may cause cracking in weld metal when electrodes are used for medium and heavy plates.
2. One-side welding defects such as hot cracking may occur with wrong welding parameter such as high welding speed.
3. Use 100% CO2 gas.

SC-81B2

Property Applications
SC-81B2 can be used for welding of 1.25%Cr-0.5%Mo heat resistant steels used for steam pipes of boilers for electric power plants and marine use, equipment for oil refining industries and high temperature synthetic chemical industries.

Characteristics on Usage
SC-81B2 is a titania type flux cored wire for all position welding. Arc stability is excellent. Spatter loss is low and slag covering is uniform with good removability.

Notes on Usage
1. Use 100% CO 2 gas.
2. All position gas shielded flux cored wire.

SC-91B3

Property Applications
SC-91B3 can be used for welding of 2.25%Cr-1.0%Mo steel used for super heat tubes and steam pipes of boilers for electric power plant and marine use, equipment for oil refining industries and high temperature synthetic chemical industries.

Characteristics on Usage
SC-91B3 is a titania type flux cored wire for all position welding. Arc stability is excellent. Spatter loss is low and slag covering is uniform with good removability.

Notes on Usage
1. Use 100% CO 2 gas.
2. All position gas shielded flux cored wire.

SW-308L

Property Applications
SW-308L Cored is designed for welding of 18%Cr-8%Ni stainless steels.

Characteristics on Usage
SW-308L Cored is a flux cored wire for all position welding to be used with CO􀍐or Argon +CO􀍐 mixed shielding gases. This wire benefits from a fast freezing slag system which assists the operator when welding out of position and performs equally as well when welding in the flat and horizontal position.

Notes on Usage
1. Use with 100% CO2or Ar + 20~25% CO2 gas.

SW-309L

Property Applications
SW-309L Cored is designed for the welding of dissimilar metals such as stainless steels and carbon steels or stainless steels and low alloy steels.

Characteristics on Usage
SW-309L Cored is a flux cored wire for all position welding to be used with CO􀍐or Argon + CO􀍐 mixed shielding gases. This wire contains a high ferrite level in its austenitic structure thus providing better weldability together superior heat and corrosion resistance. As larger amounts of alloying elements are added, it becomes suitable for the welding of dissimilar joints where dilution from ferrite steel takes place.

Notes on Usage
1. Use with 100% CO2or Ar + 20~25% CO2 gas.

SW-316L

Property Applications
SW-316L Cored is designed for the welding of low carbon 18%Cr-12%Ni-2% Mo stainless steels or for the welding of dissimilar joints of stainless steels.

Characteristics on Usage
SW-316L Cored is a flux cored wire for all position welding to be used with CO􀍐or Argon + CO􀍐 mixed shielding gases. Due to ferrite contents in the weld metals austenitic structure, it has excellent crack resistance.

Notes on Usage
1. Use with 100% CO2or Ar + 20~25% CO2 gas.

SW-316L

Property Applications
SW-316L Cored is designed for the welding of low carbon 18%Cr-12%Ni-2% Mo stainless steels or for the welding of dissimilar joints of stainless steels.

Characteristics on Usage
SW-316L Cored is a flux cored wire for all position welding to be used with CO􀍐or Argon + CO􀍐 mixed shielding gases. Due to ferrite contents in the weld metals austenitic structure, it has excellent crack resistance.

Notes on Usage
1. Use with 100% CO2or Ar + 20~25% CO2 gas.

SMAW (Electrodes)

Hyundai Brand

6013

Property Applications
S-6013.LF can be used for welding of machinery, vehicles and light structural steels, and surface dressing of heavy steel structures.

Characteristics on Usage
S-6013.LF is a low fume, high titania type electrode. Fume generation is about 20% less than conventional high titania type electrodes and whose usability is excellent in all position welding. S-6013.LF is suitable for welding of light structural steels because of its stable arc, shallow penetration and smooth welding bead.

Notes on Usage
1. Dry the electrodes at 70~100o C(158~212o F) for 30~60 minutes before use.
2. Pay attention not to exceed the range of proper currents.

7018

Property Applications
S-7018.G can be used for highly efficient-welding of 490MPa(73,000lbs/in2) class high tensile steel, such as bridges, buildings, rolling stock and machines.

Characteristics on Usage
S-7018.G is an iron powder low hydrogen type electrode of high efficiency used for welding 490MPa(73,000lbs/in2) class high tensile steel.

Notes on Usage
1. Dry the electrodes at 300~350o C(572~662o F) for 60 minutes before use.
2. Keep the arc as short as possible.

GMAW

Hyundai Brand

SM-70

Property Applications
Butt and fillet welding of steel structures such as vehicles, machinery and bridges.

Characteristics on Usage
SM-70 is a solid wire designed for all position welding by short-circuiting type transfer. As the deposition efficiency is high and penetration is deep, highly efficient welding can be performed.

Notes on Usage
1. Use with CO2/Argon+15~25% CO2 gas.
2. The Flow of quantity of shielding gas should be approximately 25 Q/min.
3. Use wind screen against wind.
4. Keep distance between tip and base metal 6~15mm for less than 250A, and 15~25mm for more than 250A of welding current.

GTAW

Hyundai Brand

ST-72

Property Applications
Butt and fillet welding of carbon steel for pressure vessels, tubes, ships.

Characteristics on Usage
1. Use welding grade Ar 100% gas.
2. All position welding and steel sheet welding can be performed quite easily.
3. Most suitable for one- side welding of tubes.

SAW

Hyundai Brand

ST-72

Property Applications
Horizontal welding of oil storage tanks, ships, bridges, pressure vessels, penstocks, boilers and structural steels.

Characteristics on Usage
Inactive, neutral type bonded flux which is applicable to all kinds of wire. Impact value of weld metal and crack resistibility are good. Slag detachability in the groove and resistance to porosity are good. Usability in horizontal fillet welding and X-ray performance are good.

Notes on Usage
1. Dry the flux at 300~350oC (572~662oF ) for 60 minutes before use.
2. Remove rust, scales, oil, paint, water, dirt and slag of tack welds from the groove to obtain sound weld metal.
3. Use welding current and speed as low as possible at the first layer of groove to avoid cracking.
4. Use welding current and speed as low as possible at the first layer of groove to avoid cracking.
5. Preheat at 50~100oC (122~212oF) according to base metal and plate thickness. Keep interpass temperature at 100~250oC (212~482oF ).

M12K & S-717

Property Applications
Multi-layer welding of structural steels, offshore structures and thick, windmill, pressure vessels.

Characteristics on Usage
Good weldability for all range of thickness of plate. Excellent impact value and crack-resistibility of welded metal. Inactive type flux is not affected by welding parameter, especially suitable for multilayer welding of thick plate.

Notes on Usage
1. Dry the flux at 300~350oC (572~662oF ) for 60 minutes before use.
2. For the first layer in groove, keep the current and speed low in the case of multi-layer welding..